Process for removing nitrogen oxides in exhaust gases

ABSTRACT

A process for removing nitrogen oxides in exhaust gases is provided. The process comprises mixing an exhaust gas generated during the chemical vapor deposition process for producing semiconductors and containing dinitrogen monoxide (N 2 O), nitrogen monoxide (NO) and nitrogen dioxide (NO 2 ) with ammonia (NH 3 ) in an amount 0.5-3 times the sum of the stoichiometric amount corresponding to nitrogen monoxide and the stoichiometric amount corresponding to nitrogen dioxide; and then contacting said mixed gas with a noble metal catalyst at a sufficiently high temperature to decompose dinitrogen monoxide, nitrogen monoxide and nitrogen dioxide. Dinitrogen monoxide (N 2 O), nitrogen monoxide (NO) and nitrogen dioxide (NO 2 ) in exhaust gases can be treated in one step. No N 2 O is produced as a by-product.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a process for removing nitrogen oxides, particularly dinitrogen monoxide (N₂O) in exhaust gases.

[0003] 2. Related Art

[0004] The selective catalytic reduction process and adsorption process are known for removing nitrogen oxides in exhaust gases discharged from incinerators, boilers and the like.

[0005] The selective catalytic reduction process involves adding a reducing agent in the presence of a catalyst to reduce nitrogen oxides (NO_(x)) into a nitrogen gas (N₂). The reducing agent preferably used is ammonia (NH₃), which selectively reduces nitrogen monoxide (NO) or nitrogen dioxide (NO₂) into a nitrogen gas (N₂) and water (H₂O). The catalyst used includes noble metal catalysts such as palladium and vanadium catalysts such as V₂O₅-WO₃-TiO₂.

[0006] On the other hand, the adsorption process involves using a molecular sieve, activated carbon, metal oxide or the like, which physically or chemically adsorbs NO and NO₂.

[0007] Nitrogen oxides in exhaust gases discharged from incinerators, boilers and the like predominantly contain nitrogen monoxide (NO) and nitrogen dioxide (NO₂) with a minor amount of dinitrogen monoxide (N₂O). For example, exhaust combustion gases from incinerators may contain 100 ppm of NO, 10 ppm of NO₂ and 10 ppm of N₂O. Therefore, conventional denitration processes put emphasis on removing nitrogen monoxide and nitrogen dioxide, but overlook removal of dinitrogen monoxide (N₂O).

[0008] A process for producing semiconductors include a step of performing chemical vapor deposition, which may refer to CVD hereinafter, on wafers. The chemical vapor deposition process sometimes discharges an exhaust gas containing dinitrogen monoxide (N₂O) in addition to nitrogen monoxide (NO) and nitrogen dioxide (NO₂).

[0009] However, the selective catalytic reduction process may produce dinitrogen monoxide (N₂O) as a by-product during reduction of nitrogen monoxide (NO) and nitrogen dioxide (NO₂) under inappropriately selected conditions. Moreover, the above-mentioned vanadium catalysts are effective to reduce nitrogen monoxide (NO) and nitrogen dioxide (NO₂) but ineffective for reducing dinitrogen monoxide (N₂O).

[0010] The adsorption process can adsorb nitrogen monoxide (NO) and nitrogen dioxide (NO₂), but not dinitrogen monoxide (N₂O). Moreover, adsorbents used in the adsorption process are readily consumed, and the consumed adsorbents must be replaced. The frequency of replacing adsorbents increases in proportion to an amount of NO and NO₂ discharged, resulting in a high running cost.

[0011] JPA No. 7826/88 discloses a process for removing dinitrogen monoxide using a palladium catalyst or the like. However, this process removes dinitrogen monoxide after nitrogen monoxide and nitrogen dioxide have preliminarily been removed. This requires a bulky apparatus for removal in at least two steps with lowered heat efficiency. Thus, there is a demand for removing dinitrogen monoxide, nitrogen monoxide and nitrogen dioxide in one step.

[0012] Therefore, an object of the present invention is to provide a process for treating an exhaust gas containing dinitrogen monoxide (N₂O), nitrogen monoxide (NO) and nitrogen dioxide (NO₂) without producing dinitrogen monoxide (N₂O) as a by-product.

SUMMARY OF THE INVENTION

[0013] The present invention provides a process for removing nitrogen oxides in an exhaust gas, comprising the steps of:

[0014] mixing an exhaust gas generated during the chemical vapor deposition process for producing semiconductors and containing dinitrogen monoxide (N₂O), nitrogen monoxide (NO) and nitrogen dioxide (NO₂) with ammonia (NH₃) in an amount 0.5-3 times a sum of a stoichiometric amount corresponding to the nitrogen monoxide and a stoichiometric amount corresponding to the nitrogen dioxide; and

[0015] contacting said mixed gas with a noble metal catalyst at a sufficiently high temperature to decompose dinitrogen monoxide, nitrogen monoxide and nitrogen dioxide.

[0016] Preferably, the present process further comprises, before said contacting step, the step of heating said exhaust gas or said mixed gas at a temperature ranging from 200° C. to said high temperature selected for said contacting step.

[0017] During said mixing step, said exhaust gas is preferably mixed with ammonia (NH₃) in an amount 0.6-2 times the sum of the stoichiometric amount corresponding to nitrogen monoxide and the stoichiometric amount corresponding to nitrogen dioxide.

[0018] Preferably, said mixed gas contains 1 mole part or more of ammonia (NH₃) per 1 mole part of an oxygen gas (O₂).

[0019] Preferably, said exhaust gas contains 1 part by weight of dinitrogen monoxide (N₂O), 0.01-3 parts by weight of nitrogen monoxide (NO) and 0.01-100 parts by weight of nitrogen dioxide (NO₂).

[0020] Preferably, said exhaust gas contains 70% by weight or more, more preferably 80% by weight or more of nitrogen gas.

[0021] Also preferably, said exhaust gas is substantially free from sulfur oxides.

[0022] Preferably, said noble metal catalyst comprises palladium or platinum.

[0023] More preferably, said noble metal catalyst comprises a carrier in a particle form and palladium or platinum supported on said carrier.

[0024] Preferably, said contacting step takes place at 250° C.-600° C.

[0025] More preferably, said contacting step takes place at 350° C.-400° C.

[0026] During said mixing step, the outlet of said exhaust gas and the outlet of said ammonia preferably face to each other.

[0027] Preferably, the present process further comprises the step of passing said mixed gas through a tortuous path after said mixing step and before said contacting step.

[0028] Preferably, the present process further comprises the step of removing excessive ammonia after said contacting step.

BRIEF DESCRIPTION OF THE DRAWINGS

[0029]FIG. 1 is a partial sectional view of a packed column suitable for carrying out the present invention.

[0030]FIG. 2 is a block diagram of a denitration apparatus suitable for carrying out the present invention.

[0031]FIG. 3 is a partial enlarged view of a reaction chamber.

PREFERRED EMBODIMENTS OF THE INVENTION

[0032] Preferred embodiments of the present invention will now be described, but are not construed to limit the same.

[0033] According to the present invention, an exhaust gas generated during the chemical vapor deposition process for producing semiconductors is treated. This exhaust gas contains dinitrogen monoxide (N₂O), nitrogen monoxide (NO) and nitrogen dioxide (NO₂). Exhaust gases generated during the chemical vapor deposition process for producing semiconductors are richer in dinitrogen monoxide than nitrogen monoxide, and typically contain 1 part by weight of dinitrogen monoxide (N₂O), 0.01-3 parts by weight of nitrogen monoxide (NO) and 0.01-100 parts by weight of nitrogen dioxide (NO₂), particularly 1 part by weight of dinitrogen monoxide (N₂O), 0.1-1.5 parts by weight of nitrogen monoxide (NO) and 0.01-100 parts by weight of nitrogen dioxide (NO₂). In contrast, exhaust gases from incinerators contain, for example, 1 part by weight of dinitrogen monoxide (10 ppm), 10 parts by weight of nitrogen monoxide (100 ppm) and 1 part by weight of nitrogen dioxide (10 ppm).

[0034] The balance of the exhaust gas may be a nitrogen gas, an oxygen gas and inevitabe impurities. For example, the exhaust gas may comprise 1 part by weight of dinitrogen monoxide (N₂O), 0.01-3 parts by weight of nitrogen monoxide (NO), 0.01-100 parts by weight of nitrogen dioxide (NO₂) and 0.01-100 parts by weight of an oxygen gas with the balance being a nitrogen gas and inevitable impurities. For example, the exhaust gas preferably contains 70% by weight or more, more preferably 80% by weight or more, most preferably 90% by weight or more of a nitrogen gas (N₂). The exhaust gas may contain 0.1-10% by weight, especially 0.5-5% by weight of an oxygen gas.

[0035] Preferably, said exhaust gas is substantially free from sulfur oxides. Alternatively, a denitration process may take place after any sulfur oxides in the exhaust gas have been removed. This is because sulfur oxides may be a catalytic poison to a noble metal catalyst.

[0036] According to the present invention, said exhaust gas is mixed with ammonia (NH₃) in an amount 0.5-3 times, preferably 0.6-2 times, more preferably 0.8-1.5 times the sum of the stoichiometric amount corresponding to nitrogen monoxide and the stoichiometric amount corresponding to nitrogen dioxide. If ammonia is added in an amount less than 0.6 times the sum, nitrogen monoxide and nitrogen dioxide can not be sufficiently removed. If ammonia is added in an amount more than 3 times the sum, the burden of removing excessive ammonia downstream of the denitration apparatus increases.

[0037] Decomposition reactions of nitrogen oxides in the presence of noble metal catalysts are shown as follows.

2N₂O→2N₂+O₂

4NO+4NH₃+O₂→4N₂+6H₂O

6NO₂+8NH₃→7N₂+12H₂O

[0038] Decomposition of dinitrogen monoxide requires neither ammonia nor an oxygen gas. However, ammonia acts as a reducing agent for nitrogen monoxide and nitrogen dioxide. An oxygen gas contributes to decomposition of nitrogen monoxide. This oxygen gas may be initially contained in the exhaust gas or added thereto if necessary.

[0039] One mole of nitrogen monoxide reacts with one mole of ammonia. Accordingly, the stoichiometric amount of ammonia corresponding to one mole of nitrogen monoxide means one mole. One mole of nitrogen dioxide reacts with 4/3 moles of ammonia. Accordingly, the stoichiometric amount of ammonia corresponding to one mole of nitrogen dioxide means about 1.33 moles. Therefore, 1.40 moles (0.6×2.33 moles) to 7.0 moles (3×2.33 moles) of ammonia should be added to treat an exhaust gas containing 1 mole of nitrogen monoxide and 1 mole of nitrogen dioxide according to the present invention.

[0040] Preferably, said mixed gas contains 1 mole part or more of ammonia (NH₃) per 1 mole part of oxygen (O₂) gas. As described above, this oxygen gas may be or may not be initially contained in the exhaust gas.

[0041] Preferably, the process of the present invention further comprises, before said contacting step, the step of heating said exhaust gas or said mixed gas at a temperature ranging from 200° C. to said high temperature selected for the contacting step. Thus, formation of ammonium nitrate can be suppressed.

[0042] During this heating step, said exhaust gas and ammonia may be introduced into a mixing chamber having a heater, in which the mixed gas may be heated. In this case, the outlet of said exhaust gas and the outlet of said ammonia preferably face to each other within the mixing chamber. This allows ammonia to vaporize to reduce the danger of explosion.

[0043] Alternatively, the exhaust gas may be preheated during this heating step, followed by addition of unheated or preheated ammonia. In this case, the process preferably further comprises the step of passing said mixed gas through a tortuous path after said mixing step and before said contacting step. The exhaust gas and ammonia can be homogeneously mixed through the tortuous path.

[0044] According to the present invention, said mixed gas is contacted with a noble metal catalyst at a sufficiently high temperature to decompose dinitrogen monoxide, nitrogen monoxide and nitrogen dioxide, after the mixing step. Thus, not only dinitrogen monoxide but also nitrogen monoxide and nitrogen dioxide are decomposed.

[0045] The sufficiently high temperature to decompose dinitrogen monoxide, nitrogen monoxide and nitrogen dioxide can be appropriately selected by those skilled in the art, depending on the noble metal catalyst. In case of a palladium catalyst or the like, this high temperature is preferably 250° C.-600° C., more preferably 350° C.-400° C. Noble metal catalysts are activated at high temperatures. Noble metal catalysts supported on alumina or the like normally resist to a temperature up to 600° C. and thus exhibit catalytic activity at a temperature of 600° C. or less. Below 250° C., the reaction rate is low and therefore unpreferable. Temperature control may be conveniently performed with a sensor such as a thermocouple. However, operation above 400° C. is not preferable in view of heat resistance of typical heated packed columns and power costs of the heater.

[0046] Said noble metal catalyst preferably comprises palladium or platinum. More preferably, it comprises a carrier in a particle form and palladium or platinum supported on said carrier. Suitable carriers include ceramics such as alumina, silica, titanium oxide, etc. Ceramics are preferably oxide ceramics, more preferably porous. The carrier in a particle form may have configurations of a sphere, a rotary ellipsoid, a cylinder defining a bore extending in an axial direction, etc.

[0047] In carrying out the present invention, the following packed column can be used, for example.

[0048]FIG. 1 is a partial sectional view showing an embodiment of a packed column 1 suitable for carrying out the present invention.

[0049] The packed column has a vertically extending cylinder and a horizontal diaphragm 3 with a plurality of vent holes. A heater 2 is embedded within the sidewall of the cylinder. The diaphragm 3 partitions the inside of the cylinder into upper and lower portions. A packed chamber 4 packed with a noble metal catalyst is provided in the upper portion of the cylinder partitioned by the diaphragm 3, while a gas mixing chamber 5 is provided in the lower portion of the cylinder. An exhaust gas inlet tube 6 and an ammonia inlet tube 7 open into the gas mixing chamber 5. The outlet 6 a of the exhaust gas inlet tube 6 and the outlet 7 a of the ammonia inlet tube 7 face to each other.

[0050] An exhaust tube not shown communicating with the packed chamber 4 extends from the outlet of the packed column to the outside of the packed column 1 to reach a water scrubber column.

[0051] The packed chamber 4 is packed with a Pd catalyst as a treating agent. The Pd catalyst 8 preferably comprises 0.5-1.0% by weight of Pd supported on a porous material such as alumina based on Al₂O₃. The shape of the porous material carrying Pd is not critical in principle, but preferably spherical in view of handling. The sphere preferably has a diameter of 3-6 mm. If the diameter exceeds 6 mm, it may be difficult to ensure a preferred, sufficient surface area per unit volume for reaction contact. If the diameter is less than 3 mm, the catalyst unpreferably has high resistance to air permeability. The Pd catalyst is used at 250° C.-600° C., preferably 350° C.-400° C.

[0052] In carrying out the present invention, an exhaust gas containing nitrogen oxides is introduced into the gas mixing chamber 5 in the packed column 1 from the exhaust gas inlet tube 6 and mixed with ammonia introduced from the ammonia inlet tube 7. The temperature of the gas phase in the gas mixing chamber 5 where the exhaust gas and NH₃ are mixed is preferably 200° C. or more. Temperatures lower than 200° C. are not preferred because a reaction for producing powdery NH₄NO₃ is more liable to occur between NO₂ and NH₃ when the content of nitrogen oxides, particularly NO₂ is high. NH₄NO₃ is solid at ambient temperatures. If a powder is produced and accumulated in the packed column 1, it may block a tubing, which necessitates another device for removing the powder together with maintenance thereof. In addition, NH₄NO₃ is a hazardous material (Class 1 in Art. 2 of the Japanese Fire Protection Law), which needs special care for handling for safety reasons. If a large amount of NH₄NO₃ powder accumulates in the packed column 1, this situation by itself would involve a great danger of accident. NH₄NO₃ decomposes at about 210° C. to produce water and N₂O. At a temperature of 200° C. or more, formation of NH₄NO₃ can be effectively suppressed. Therefore, the exhaust gas and NH₃ may be mixed at a temperature of 200° C. or more.

NH₄NO₃→N₂O+2H₂O

[0053] The exhaust gas and ammonia may be introduced into the mixing chamber 5 in either down flow or up flow.

[0054] When the packed column 1 described above is used, the exhaust gas and ammonia are mixed together in the mixing chamber 5 and gradually moved into the packed chamber 4, where they come into contact with a Pd catalyst at 350° C.-400° C. for oxidation-reduction reactions.

[0055] The mixed gas having passed through the packed chamber 4 runs through an exhaust tube not shown extending therefrom to reach a water scrubber column, where an excessive, unreacted NH₃ gas is removed. Then, only an environmentally safe gas can be diffused into the atmosphere.

[0056] In carrying out the present invention, a denitration apparatus 10 shown in FIG. 2 can also be used, for example.

[0057] In FIG. 2, the denitration apparatus 10 has a preheating chamber 12 and a reaction chamber 20. The preheating chamber 12 is preferably packed with ceramic particles 14 to enhance heat transfer. The preheating chamber 12 is connected to a chemical vapor deposition apparatus 30 for producing semiconductors via a line 36. An exhaust gas discharged from the chemical vapor deposition apparatus 30 is introduced into the lower portion of the preheating chamber 12 via a pump 32 and heated to 200° C. or more, for example.

[0058] The preheating chamber 12 is connected to an inlet of the reaction chamber 20 via a line 16. An ammonia line 18 is also connected to the inlet of the reaction chamber 20. As shown in FIG. 3, a baffle 22 for meandering the gas is preferably provided at the inlet of the reaction chamber 20. The exhaust gas and ammonia can be homogeneously mixed through this tortuous path.

[0059] The reaction chamber 20 is packed with a noble metal catalyst 24, which may be similar to the noble metal catalyst as shown in FIG. 1. The reaction chamber 20 is equipped with a heater not shown, which can heat the noble metal catalyst at a high temperature such as 250° C.-600° C., for example. The heater may be provided within the sidewall of the reaction chamber 20 in the same manner as shown in FIG. 1, for example. Nitrogen oxides in the exhaust gas are decomposed within the reaction chamber 20.

[0060] The gas having passed through the reaction chamber 20 is introduced into a scrubber column via a line 26 to remove an excessive, unreacted NH₃ gas.

[0061] The following examples illustrate the present invention, but are not construed as limiting the same.

EXAMPLES Reference examples 1-6, 13 and 14

[0062] A packed column 1 or mini-column having a diameter of 25 mm made from quartz and equipped with a ceramic heater 2 in its sidewall as shown in FIG. 1 was prepared, which includes a gas mixing chamber 5 in the lower stage and a packed chamber 4 having a bed height of 100 mm in the upper stage. The packed chamber 4 was packed with a Pd catalyst 8 comprising 0.5% by weight of Pd supported on alumina in a particle form of 3-6 mm in a particle diameter, and the mixing chamber and packed chamber were each fitted with a thermocouple temperature sensor not shown.

[0063] The inside of the packed column was heated from the sidewall by the ceramic heater to maintain the temperature of the gas phase in the gas mixing chamber 5 at 265° C.-290° C. and the temperature of the packed chamber 4 at 350° C.-360° C.

[0064] A gas containing any one of nitrogen oxide gases selected from NO, NO₂ and N₂O and O₂ was introduced into the gas mixing chamber 5 via an exhaust gas inlet tube 6. A nitrogen gas was used as a carrier. Namely, nitrogen oxide and oxygen gases were added to a nitrogen gas as a carrier. In Table 1, the concentrations of nitrogen oxide and oxygen gases are expressed as percent by weight based on the total of nitrogen oxide, oxygen and nitrogen gases. The total flow rate of the exhaust gas was 408 sccm, and SV was 500 hr⁻¹.

[0065] Similarly, an NH₃ gas was introduced via an ammonia inlet tube 7. The carrier for the ammonia gas was a nitrogen gas, and ammonia concentrations in Table 1 are expressed as percent by weight based on the total of ammonia gas and the nitrogen gas. The inlet gas concentrations of nitrogen oxides were about 1%, and the influent amount of the NH₃ gas was at least equimolar to O₂ in the exhaust gas introduced via the exhaust gas inlet tube 6.

[0066] At the column outlet from which an exhaust tube extends to the outside of the mini-column, gas concentrations of nitrogen oxides were analyzed. Analytical methods used were the reactor tube method for NO, NO₂ and NH₃, the GC-MS method for N₂O, and the GC-TCD method for O₂. Analytical results of gases at the outlet after gas circulation for 2 hours are shown in Table 1, revealing that all of NO, NO₂ and N₂O have been removed to levels below detection limits. No deposition of NH₄NO₃ was observed at the inner face of the gas mixing chamber 5 where the gas phase was maintained at a temperature of 200° C. or more. However, some deposition of NH₄NO₃ was observed at places where the temperature of the gas phase was lowered to 80° C.-95° C. TABLE 1 Controlled temperature Inlet gas concentration Outlet gas concentration Reference Treatment of treatment NO NO₂ N₂O O₂ NH₃ NO NO₂ N₂O O₂ NH₃ example agent bed (° C.) (%) (%) (%) (%) (%) (ppm) (ppm) (ppm) (%) (ppm) 1 Pd/Al₂O₃ 350 0.95 — — 3.1 3.8 <1 <1 <1 <0.1 10500 2 Pd/Al₂O₃ 350 0.95 — — 3.1 4.9 <1 <1 <1 <0.1 21000 3 Pd/Al₂O₃ 350 — 0.93 — 3.4 3.9 <1 <1 <1 <0.1 3900 4 Pd/Al₂O₃ 350 — 0.89 — 2.7 4.6 <1 <1 <1 <0.1 3500 5 Pd/Al₂O₃ 350 — — 0.96 2.8 3.2 <1 <1 <1 <0.1 <1 6 Pd/Al₂O₃ 350 — — 0.96 3.1 4.3 <1 <1 <1 <0.1 10000 13 Pd/Al₂O₃ 350 0.95 0.93 0.96 3.1 3.8 <1 <1 <1 <0.1 <1 14 Pd/Al₂O₃ 350 0.034 0.39 0.11 5.2 5.8 <1 <1 <1 <0.1 <4800

Reference examples 7-11

[0067] In Reference examples 7-11, the same experimental equipment and the same catalyst as in References 1-6 and 13 were used. However, the influent amount of NH₃ gas was less than an equimolar amount to O₂ in the exhaust gas introduced via the exhaust gas inlet tube 6.

[0068] Analytical results of gases at the outletafter gas circulation for 2 hours are shown in Table 2. All of NO, NO₂ and N₂O were detected at high concentration values. These results show a remarkable decrease in treatment efficiency. TABLE 2 Controlled temperature Inlet gas concentration Outlet gas concentration Reference Treatment of treatment NO NO₂ N₂O O₂ NH₃ NO NO₂ N₂O O₂ NH₃ example agent bed (° C.) (%) (%) (%) (%) (%) (ppm) (ppm) (ppm) (%) (ppm) 7 Pd/Al₂O₃ 350 0.95 — — 4.2 1.9 1000 750 7700 2.0 <1 8 Pd/Al₂O₃ 350 0.95 — — 2.9 2.4 460 180 8400 <0.1 <1 9 Pd/Al₂O₃ 350 — 0.93 — 3.1 2.1 200 180 1500 2.9 <1 10 Pd/Al₂O₃ 350 — 0.93 — 6.0 2.3 300 200 2600 2.4 <1 11 Pd/Al₂O₃ 350 — — 0.96 3.2 2.3 200 240 14200 0.3 <1

Reference example 12

[0069] In Reference example 12, the same experimental equipment as in References 1-6 and 13 was used. However, the denitration catalyst used was a commercially available V₂O₅-WO₃-TiO₂ catalyst in the form of fragments having a particle diameter of 4-7 mm. The influent amount of NH₃ gas was at least equimolar to O₂ in the exhaust gas introduced with nitrogen oxide via the exhaust gas inlet tube 6.

[0070] Analytical results of a gas at the outlet after gas circulation for 2 hours are shown in Table 3. Both of NO and NO₂ were below detection limits. However, N₂O as a by-product was detected in a gas at the outlet. TABLE 3 Controlled Inlet gas temperature concentration Outlet gas concentration Reference Treatment of treatment NO₂ O₂ NH₃ NO NO₂ N₂O O₂ NH₃ example agent bed (° C.) (%) (%) (%) (ppm) (ppm) (ppm) (%) (ppm) 12 V₂O₅—WO₃—TiO₂ 350 0.92 2.8 4.4 <1 <1 270 <0.1 20600

[0071] According to the present invention, dinitrogen monoxide (N₂O), nitrogen monoxide (NO) and nitrogen dioxide (NO₂) in exhaust gases can be treated in one step without producing N₂O as a by-product. 

What is claimed is:
 1. A process for removing nitrogen oxides in an exhaust gas, comprising the steps of: mixing an exhaust gas generated during the chemical vapor deposition process for producing semiconductors and containing dinitrogen monoxide (N₂O), nitrogen monoxide (NO) and nitrogen dioxide (NO₂) with ammonia (NH₃) in an amount 0.5-3 times a sum of a stoichiometric amount corresponding to the nitrogen monoxide and a stoichiometric amount corresponding to the nitrogen dioxide; and contacting said mixed gas with a noble metal catalyst at a sufficiently high temperature to decompose dinitrogen monoxide, nitrogen monoxide and nitrogen dioxide.
 2. The process of claim 1 further comprising, before said contacting step, the step of heating said exhaust gas or said mixed gas at a temperature ranging from 200° C. to said high temperature selected for said contacting step.
 3. The process of claim 1 wherein said exhaust gas is mixed with ammonia (NH₃) in an amount 0.6-2 times the sum of the stoichiometric amount corresponding to the nitrogen monoxide and the stoichiometric amount corresponding to the nitrogen dioxide during said mixing step.
 4. The process of claim 1 wherein said mixed gas contains 1 mole part or more of ammonia (NH₃) per 1 mole part of an oxygen gas (O₂).
 5. The process of claim 1 wherein said exhaust gas contains 1 part by weight of the dinitrogen monoxide (N₂O), 0.01-3 parts by weight of the nitrogen monoxide (NO) and 0.01-100 parts by weight of the nitrogen dioxide (NO₂).
 6. The process of claim 1 wherein said exhaust gas contains 70% by weight or more of a nitrogen gas (N₂).
 7. The process of claim 1 wherein said exhaust gas is substantially free from sulfur oxides.
 8. The process of claim 1 wherein said noble metal catalyst comprises palladium or platinum.
 9. The process of claim 1 wherein said noble metal catalyst comprises a carrier in a particle form and palladium or platinum supported on said carrier.
 10. The process of claim 1 wherein said contacting step takes place at 250° C.-600° C.
 11. The process of claim 1 wherein said contacting step takes place at 350° C.-400° C.
 12. The process of claim 1 wherein the outlet of said exhaust gas and the outlet of said ammonia face to each other during said mixing step.
 13. The process of claim 1 further comprising the step of passing said mixed gas through a tortuous path after said mixing step and before said contacting step.
 14. The process of claim 1 further comprising the step of removing excessive ammonia after said contacting step. 